There are many factors to affect the performance of rock wool, but acidity coefficient, as an important index, shall affect the quality of rock wool directly.
Acidity coefficient affects the melting of rock wool directly. A lot of experiments show that the acidity coefficient of rock wool is lower, the restriction of rock wool to melting will lower. The temperature to melt the rock wool with acidity coefficient of 2.0 is 130℃ to 150℃ higher than that to melt the rock wool with acidity coefficient of 1.0, which shows that the rock wool material that has high melting difficulty with high acidity coefficient shall need more fuel correspondingly and has very high requirements to equipment and refractory materials.
Acidity coefficient shall affect the water resistance of rock wool. When the acidity coefficient of rock wool is higher, the water resistance will be higher, and when the acidity coefficient is lower, the water resistance will lower greatly. If the acidity coefficient of rock wool board is too low, it will break fiber, pulverize and at last lose the due strength to sink and pile up by suffered from hydrolysis in grid structure.
There is one more point that acidity coefficient affects the thermal stability of rock wool. Rock wool is an incombustible material. The research of its heat setting is mainly to see whether the rock wool board can maintain its shape normally as it is heated, especially the fire-insulated effect of material used. The rock wool with very low acidity coefficient will shrink sharply at very high temperature, while the rock wool board with high acidity coefficient will have less effect change to its shape at very high temperature.
락울성능에 영향주는 요소는 많지만 산도계수는 중요한 지표로서 락울질량에 직접 관계됩니다.
산도계수는 락울의 용제에 직접적인 영향을 주며 대량의 실험을 통해 알아본데 따르면 락울의 산도계수가 낮을 수록 락울이 용제에 대한 한계가 낮아지며 산도계수가 2.0인 락울의 용제는 산도계수가 1.0인 락울용제의 온도보다 130도에서 150도 높습니다. 이는 고산도계수의 용제난도 락울재료는 연료를 상대적으로 증가하게 되며 설비와 내화재료에 아주 높은 요구가 있음을 말해줍니다.
산도계수는 락울의 내수성에 영향주며 락울의 산도계수가 높을 수록 내수성이 높고 산도계수가 낮을 수록 내수성이 감소됩니다. 락울판의 산도계수가 너무 낮으면 오랜 시간 뒤 격자구조중 가수분해작용을 받아 섬유가 단열되고 분화되며 마지막에는 강도를 잃고 퇴적되게 됩니다.
또 하나는 산도계수는 락울의 열온정성에 영향을 줍니다. 락울은 불연재료이며 열온정성을 연구할 때 주요하게 온도작용을 받을 때 락울판이 정상적인 형태를 유지할 수 있는지 특히는 방화작용에 대해 연구하게 됩니다. 산도계수가 아주 낮은 락울은 온도가 높은 정황하에 급격히 수축되며 산도계수가 높은 락울판은 높은 온도에서도 형태변화가 크지 않습니다.